Documents Similar To Astm c ASTM C – Uploaded by. Alejandro Pinto. ASTM C Uploaded by. Nelson. BS EN Uploaded by. ASTM C Measurement of Rate of Absorption of Water by Hydraulic-Cement Concretes. Lab ID: Use This method is intended to determine the. caused by the deterioration mechanism by the means of the ASTM C C 04 results were then analyzed to validate the applicability of the.

Author: Kazrakus Dutaur
Country: Mali
Language: English (Spanish)
Genre: Personal Growth
Published (Last): 17 January 2018
Pages: 40
PDF File Size: 5.70 Mb
ePub File Size: 19.8 Mb
ISBN: 547-2-62258-872-1
Downloads: 84914
Price: Free* [*Free Regsitration Required]
Uploader: Dobar

This test method is used to measure the water absorption rate of both the concrete surface and interior concrete. If you need more info or have any questions, please note the Lab ID number and contact us at: In general, the rate of absorption of concrete at the surface differs from the rate of absorption of a sample taken from the interior. Time for Results Please contact a CTLGroup chemical services representative or Project Manager to discuss your individual project needs and testing response times.

No other units of measurement are included in this standard. This test method is used to measure the water absorption rate of both the concrete surface and interior concrete.

Referenced Documents purchase separately The documents listed below are referenced within the subject standard c185 are not provided as part of the standard. Historical Version s – view previous versions of standard. In unsaturated concrete, the rate of ingress of water asttm other liquids is largely controlled by absorption due to capillary rise. The following information should be provided to be included in asrm report: Water absorption is also strongly affected by the moisture condition of the concrete at the time of testing.

  LINQ UNLEASHED FOR C# PDF

It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

The exterior surface is often subjected to less than intended curing and is exposed to the most potentially adverse conditions. The average of test results on at least 2 specimens shall constitute the test result.

The specimen is conditioned in an environment at a standard relative humidity to induce a consistent moisture condition in the capillary pore system. In this test method, only one surface asrm exposed to water at room temperature while the other surfaces are sealed simulating water absorption in a member that is in contact with water on one side only.

Test Method Con the other hand, is used to estimate the maximum amount of water that can be absorbed by a dry specimen and therefore provides a measure of the total, water permeable pore space.

The exposed surface of the specimen is immersed in water and water ingress of unsaturated concrete is dominated by capillary suction during initial contact with water.

Print and complete c11585 following order form. Instructions Provide at least two concrete cylinders or cores. Order Form 2 Email complete form to contact listed below. The core is drilled vertically or horizontally.

ASTM C Rate of Absorption of Water by Hydraulic Cement | CTLGroup

By drilling a core and cutting it transversely at selected depths, the absorption can be evaluated at different distances from the exposed surface. Link to Active This link will always route to the current Active version of the standard. The surface to be exposed during testing shall not be marked or otherwise disturbed in such a manner as may modify the absorption rate of the specimen.

  1774 KK KAYNARCA ANTLAMAS PDF

The test surfaces shall be at the same distance from the original exposed surface of the concrete. Use This method is intended to determine the susceptibility of an unsaturated concrete to the penetration of water.

In general, the rate of absorption of concrete at the surface differs from the rate of absorption of a sample taken from the interior.

ASTM C1585 – 13

The exterior surface is often subjected to less than intended curing and is exposed to the most potentially adverse conditions. If you need more info or have any questions, please note the Lab ID number and contact us at:.

When cores are taken, they should satm marked so that the surface to be tested relative to the original location in the structure is clearly indicated. Privacy Policy Sensors Sitemap. The core is drilled vertically or horizontally. By drilling a core and cutting it transversely at selected depths, the absorption can be evaluated at different distances from the exposed surface.